What are the other names and ingredient properties of IncoloyA286?
IncoloyA286/alloyA286
Incoloy A286 is a Fe-Ni-Cr-based precipitation hardening deformed high-temperature alloy with a service temperature range of -253°C to 650°C. In order to increase the strength, further improve the purity of the alloy, reduce the content of sulfur, gases, and trace elements, and adjust The heat treatment system has good high and low temperature strength and long-term stability, good resistance to corrosion and thermal deformation, and has good processing plasticity and satisfactory welding performance. It is suitable for manufacturing high-temperature load-bearing parts of aeroengines that work for a long time below 650°C. Such as press discs, rotor blades and fasteners, etc. The alloy can produce deformed products of various shapes, such as discs, forgings, plates, rods, wires and rings, etc.
Incoloy A286 corresponding brands: national standard: x6nicrtimovb25-15-2, German standard 1.4980, 1.4944, x5nicrti26-15, American standard S66286, 660, incoloy A286.
Incoloy A286 chemical composition:
Nickel Ni: 24-27,
Chromium Cr: 13.5-16,
Molybdenum: ≤1.0-1.5,
Boron B: ≤0.001-0.01,
Iron Fe: balance,
Aluminum Al: ≤0.40,
Titanium TI≤1.75-2.35,
Carbon C: ≤0.08, Manganese Mn: ≤ 2.0, Silicon Si: ≤1.0, Vanadium V: ≤0.5, Sulfur S: ≤0.03, Copper Cu: ≤0.25.
Incoloy A286 physical properties: density 7.93 g/cm3, melting point 1364-1424°C, tensile strength Rm N/mm2: 950, yield strength RP0.2N/mm2: 680, elongation A5 %: 28.
Incoloy A286 supply status: hot-rolled and forged rods are generally supplied without heat treatment, polished and machined, plates are supplied after solid solution, pickling, flattening and trimming, and tubes are supplied after solid solution and pickling.
Incoloy A286 main features: high yield strength, creep strength below 650°C, good processing plasticity and satisfactory welding performance.
Application of Incoloy A286: This alloy is an alloy material with high high-temperature strength and high-temperature oxidation resistance. It is widely used in manufacturing parts and various fasteners for aerospace engines and industrial gas turbines. It is also widely used in automobile engines.