EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm

EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm
EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm
EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm
EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm
EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm

EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm

Alloy special steel Chemical composition of steel 30CrNiMo8 (1.6580), Standards of steel 30CrNiMo8 (1.6580) Mechanical Properties of steel 30CrNiMo8 (1.6580) Equivalent grades of steel 30CrNiMo8 (1.6580) Tensile Strength, Elongation, Proof strength, Hardness

Send Inquiry

Chat Now

As a leading supplier and manufacturer in China, GNEE Steel provides cost-effective nickel-based alloy products.

Send E-mail: ss@gneesteel.com

Product Introduction

Gnee Super Alloy (Tianjin) Co., Ltd. is one of the most professional manufacturers and suppliers of en10250 din 30crnimo8 1.6580 30cnd8 rough turned alloy steel round bar od 280mm in China. If you're going to wholesale high quality en10250 din 30crnimo8 1.6580 30cnd8 rough turned alloy steel round bar od 280mm made in China, welcome to get free sample from our factory. Good service and reasonable price are available.

EN10250 DIN 30CrNiMo8 1.6580 30CND8 Rough Turned Alloy Steel Round Bar OD 280mm

Description

OD:	16-500mm	Length:	6m 9m 12m
Surface:	Black And Bright	Type:	Hot Rolled
Steel Grade:	Alloy Steel	Technique:	Hot Rolled,Forged
Application:	Structural Steel Bar,Die Steel Bar,Tool Steel Bar	Standard:	ASTM,DIN,AISI,JIS
Shape:	Round	Product Name:	AISI4340 Qt Alloy Steel Round Bars
Surface Treatment:	Black/Peeling/Polishing/Machined
High Light:	OD 280mm forged steel round bar , 30CrNiMo8 forged round bar , OD 280mm steel round bar

30CrNiMo8|DIN 1.6580 is a heat treatable steel which has at least 1.8%Cr,1.8%Ni,and 0.3%M0 as strengthening alloy elements.It is usually supplied with quenched and tempered condition with a typical tensile strength of 1100 -1300 N/mm². 30CrNiMo8 steel is used for automotive and general components which requires high demands on strength and toughness and good hardenability.It is especially suitable for heavy duty parts in the aviation, automotive and military industries.

1.Supply Form & Size & Tolerance

Hot rolled bar:Φ6-Φ130mm,Length:3000-10000mm

Hot Forged round bar:Φ130-Φ1000mm,Length:3000-10000mm

Flat bar/Blcoks:Thickness :120-800mm xWidth:120-1500mm,Length:2000-6000mm

Surface Finish	Tolerance
Black For Forged condition	(0,+5mm)
Black For Rolled condition	(0,+1mm)
Rough Turned	(0,+3mm)
Grinding	Best h9
Polished	Best h11
Peeled	Best H11
Cold Drawn	Best H11

2.Chemical Composition

Standard	Grade	C	Si	Mn	P	S	Cr	Ni	Mo
EN10083	30CrNiMo8/1.6580	0.26-0.34	≤0.4	0.5-0.8	≤0.025	≤0.035	1.8-2.2	1.8-2.2	0.3-0.5
EN10250	30CrNiMo8/1.6580	0.26-0.34	≤0.4	0.3-0.6	≤0.035	≤0.035	1.8-2.2	1.8-2.2	0.3-0.5

3.Relevant Standards

USA	UK	France	Italy
A320L43	823M30	30CND8	30CrNiMo8

4. Mechanical Property

Diameter d mm	≤ 16	16-40	40-100	100-160	160-250
Yield Strength Mpa	≥900	≥800	≥700	≥600	≥550
Tensile Strength Mpa	1100-1300	1000-1200	900-1100	800-950	750-900
Elongation, %	≥10	≥11	≥12	≥13	≥14
Reduction of area ,%	≥45	≥50	≥55	≥60	≥60
impact,J	≥35	≥40	≥45	≥45	≥45
Hardness,HB	331-380	298-359	271-331	240-286	225-271

5.Forging

Heat the temperature between 1050℃-1150℃,hold suitable time for the steel to be thoroughly heated.Reheat the steel once temperature below 850°C. 30CrNiMo8 steel has good forging characteristics,but crack is easily occured when improper cooling way after forged,so it should be cooled as slowly as possible in the furnace or in sand after forged.

6.Heat Treatment

Normalizing:870℃-880℃,Cool in air

Soft Annealing:650℃-700℃,Cooling 10℃ per hour in furnace,max. 248 HB

Stress Relieving:50°C under the temperature of tempering

Hardening:830 – 860°C,oil or polymer,840-850°C,water

Tempering:540°C – 660°C, cool in still air

7.Jominy Test-Hardenability

HRC-mm	Type	1.5	3	6	7	9	11	13	15	20	25	30	35	40	45	50
MIN	+H	48	48	48	48	47	47	47	46	46	45	45	44	44	43	43
MAX	+H	56	56	56	56	55	55	55	55	55	54	54	54	54	54	54
MIN	+HH	51	51	51	51	50	50	50	49	49	48	48	47	47	47	47
MAX	+HH	56	56	56	56	55	55	55	55	55	54	54	54	54	54	54
MIN	+HL	48	48	48	48	47	47	47	46	46	45	45	44	44	43	43
MAX	+HL	53	53	53	53	52	52	52	52	52	51	51	51	51	50	50

Heat treatment conditions

+A	Soft annealed
+AC	Annealed to achieve spheroidization of the carbides
+AR	As rolled
+AT	Solution annealed
+C	Cold drawn / hard
+CR	Cold rolled
+FP	Treated to ferrite-pearlite structure and hardness range
+I	Isothermal annealing
+LC	Cold drawn / soft
+M	Thermo mechanical rolling
+N	Normalized
+NT	Normalized and tempered

+P	Precipitation hardened
+PE	Peeled
+QA	Air quenched and tempered
+QL	Liquid quenched and tempered
+QT	Quenched and tempered
+S	Treated to improve shearability
+SH	As rolled and turned
+SR	Cold drawn and stress relieved
+T	Tempered
+TH	Treated to hardness range
+WW	Warm worked
+U	Untreated

Alloy special steel
Chemical composition of steel 30CrNiMo8 (1.6580), Standards of steel 30CrNiMo8 (1.6580)
Mechanical Properties of steel 30CrNiMo8 (1.6580) Equivalent grades of steel 30CrNiMo8 (1.6580)
Tensile Strength, Elongation, Proof strength, Hardness