Inconel 601 chemical composition:
Carbon C: ≤0.10,
Chromium Cr: 21~25,
Nickel Ni: 58~63,
Aluminum AL: 1.0~1.7,
Iron Fe: excess,
Manganese Mn: ≤1.50,
Silicon Si: ≤0.50,
Phosphorus P: ≤0.020,
Sulfur S: ≤0.015.
Inconel 601 physical function:
Density 8.11g/cm3, melting point 1320-1370℃
Inconel 601 mechanical function:
Tensile strength (MPA): RmN/mm2; annealing treatment 650 degrees solid solution treatment 600 degrees,
Yield strength (MPA): RP0.2N/mm2; annealing treatment 300-solid solution treatment 240,
Elongation: A5%, 30-30,
Brinell hardness HB: annealing treatment.-solid solution treatment ≤220.
Inconel 601 features:
1. Excellent oxidation resistance at high temperature
2. Good carbonization resistance
3. Good oxidation resistance in sulfur-containing atmosphere
4. Good mechanical properties at room temperature and high temperature
5. Good resistance to stress corrosion cracking. Due to the control of carbon content and grain size, 601 has a higher creep rupture strength, so 601 is recommended for use in areas above 500°C.
Inconel 601 application areas:
Mainly used in heating equipment, chemical industry, environmental pollution control, and power industry. Such as heat treatment equipment and components, various industrial furnace tubes, sleeves, flame nozzles, electric heating elements, resistance wire sleeves, condenser tubes for chemical industry, and heat-resistant and corrosion-resistant parts for glass industry.
Inconel 601 supply varieties:
Inconel 601 plates, Inconel 601 bars, Inconel 601 pipes, Inconel 601 strips, Inconel 601 wires, Inconel 601 pipe fittings, Inconel 601 forgings, etc.