Gnee Super Alloy (Tianjin) Co., Ltd. is one of the most professional manufacturers and suppliers of esr grade seamless steel pipe sae 4130 / en 41b od 155mm x id 110mm hollow pipe in China. If you're going to wholesale high quality esr grade seamless steel pipe sae 4130 / en 41b od 155mm x id 110mm hollow pipe made in China, welcome to get free sample from our factory. Good service and reasonable price are available.

ESR Grade Seamless Steel Pipe SAE 4130 / En 41B OD 155mm X ID 110mm Hollow Pipe

Description

ESR Grade SAE 4130 / En 41B OD 155mm X ID 110mm Seamless Hollow Pipe

AISI 4130 alloy steel is a medium carbon, low alloy steel in ASTM A29 standard. ASTM 4140 steel is also commonly referred to as a chromoly steel, or chrome moly steel, containing nominally 0.28-0.33% Carbon, 0.8-1.1% Chromium and 0.15-0.25% Molybdenum. It is similar to 4140 steel which has a higher carbon level (0.28-0.33%), giving 4130 material improved weldability, at the expense of through thickness strength. With the proper heat treatment it is also readily machined. Annealing ASTM 4130 alloy steel offers excellent ductility. AISI 4130 steel is usually supplied as round bar commonly in the hardened and tempered condition.

AISI/SAE 4130 steel grade is a versatile alloy with good atmospheric corrosion resistance and reasonable strength up to around 315º C (600º F). It shows good overall combinations of strength, toughness and fatigue strength.

As one of leading supplier of 4130 steel alloy material, Mittel is reliable in 4130 round bar and steel plate materials. Please check below technical data of ASTM 4130 steel material.

AISI Alloy 4130 Steel Supply Range

4130 Steel Round Bar: diameter 8mm – 3000mm
4130 Steel Plate/Flat Bar: thickness 10mm – 1500mm x width 200mm – 3000mm
4130 Steel Tube: outer diameter 4mm to 800mm

Surface Finish: Black, Rough Machined, Peeled, Turned or as per given requirements.

RFQ OF 4130 STEEL

AISI 4130 Steel Specification and Relevant Standards

ASTM 4130 Steels And Equilvalents Chemical Composition

4. AISI Alloy 4130 Steel Mechanical Properties

Steel 4130 Physical Properties

Density (lb / cu. in.) 0.283

Specific Gravity 7.8

Specific Heat (Btu/lb/Deg F – [32-212 Deg F]) 0.114

Melting Point (Deg F) 2610

Thermal Conductivity 22.3

Mean Coeff Thermal Expansion 7

Modulus of Elasticity Tension 29

AISI 4130 Steel Mechanical Properties

Thermal Properties

Forging of 4130 Alloy Steel

ASTM A29 Grade 4130 steel should be forged between 1230 and 950 º C (2250 and 1750 º F). The lower the finishing temperature from forging, the finer will be the grain size. If the 4130 alloy steel is forged at too low a temperature, there is a risk of the formation of a non-uniform structure in certain areas of the forged part, necessitating a normalizing treatment, prior to further heat treatment.

RFQ OF 4130 STEEL

AISI 4130 Steel Grade Heat Treatment

Annealing of 4130 steels

Annealing of 4130 steel forgings may be carried out by transferring the part straight from the forging operation to a furnace held at a suitable temperature, around 860º C (1575 º F) for annealing, holding for a suitable time then furnace cooling. In this way a structure suitable for machining may be obtained. This treatment is best used for parts with simple shapes. If the 4130 forging is such that some sections will finish much colder than others then a uniform structure will not be obtained and for best results a spheroidizing anneal at around 750 º C (1380 º F) may be used. It is safe to say that experience alone will decide the best type of annealing treatment to be used prior to machining.

It should then be cooled in the furnace at a rate of less than 50 F per hour down to 900 F, followed by air cooling from 900 F.

Normalizing of Alloy Steel 4130

The nominal normalizing temperature for 4130 is 900 º C (1650 º F) followed by the 1600 F soak and oil quench, but production experience may necessitate a temperature either 50 º F (10 º C) above or below this figure. In fact when forgings are normalized before, for example, carburizing or hardening and tempering, the upper range of normalizing temperatures is used. When normalizing is the final heat treatment, the lower temperature range is used.

Hardening of AISI 4130 Alloy Steel

The steel 4130 should be austenitized – i.e. all micro constituents transformed to austenite – at 1500 to 1600 º F (815 to 870 º C). The actual austenitizing temperature is a function of chemical composition within the analysis range, section size and cooling method. Smaller sections of 4130 might be quenched in oil, heavier sections in water.

Tempering of 4130 Steel

The actual tempering temperature will depend on what required properties are needed. Alloy steel 4130 is tempered at between 398 ºC -565 ºC (750 F and 1050 F), depending upon the strength level desired. The lower the tempering temperature the greater the strength. However, tempering should not be carried out between 200 – 420 ºC (400 – 790 º F) to avoid the danger of embrittlement.

Machinability

The AISI 4130 alloy is readily machinable by conventional methods. Simple shapes might be machined following a normalizing treatment, whereas more complex shapes will require annealing. However, machining becomes difficult when the hardness of the 4130 steel is increased.

Welding

AISI 4130 steel is also good in weldability, and the 4130 alloy may be welded by any commercial method. The material may require a post-weld stress relief heat treatment in certain instances.

Low-hydrogen electrodes are recommended together with preheat at 150 – 260 º C (300 – 500 º F) to be maintained during welding, Cool slowly and stress relieve where possible.

Application of 4130 Steel

AISI 4130 steel alloy is used primarily in the construction of commercial and military aircraft and ground support systems.

Alloy steel 4130 is an intermediate strength material. Lighter gauges offer lighter weight but still maintain great strength, making it excellent for auto racing and aerospace.

This low alloy 4130 steel is widely used in many applications, and some typical application areas are as follows:

Commercial aircraft, aircraft engine mounts

Military aircraft

Automotive

Machine tools

Hydraulic tools

Auto racing

Aerospace

Oil and gas industries – as forged valve bodies and pumps

Agricultural and defense industries etc.

Mittel steel is one of reliable supplier of 4130 steel materials for your different applications. Contact us for a quote or any technical queries. We'd like to hear from you.

Hot Tags: esr grade seamless steel pipe sae 4130 / en 41b od 155mm x id 110mm hollow pipe, China esr grade seamless steel pipe sae 4130 / en 41b od 155mm x id 110mm hollow pipe suppliers, 1 4509 1 4510 Pipes And Tubes, SS410 Stainless Steel Pipe, Stainless Steel High Pressure Pipe, Slip On Flanges, Inconel 625 Alloy Steel Plate, 420J1 420J2 316 Stainless Pipe